梧州耐高温不锈钢管新闻
|
用途
|
日本
|
美国
|
德国
|
中国
|
|
锅炉、热交换器用碳素钢钢管
|
JIS G3461
|
STB340
(STB35)
|
ASTM A179
A192
|
DIN 17175 ST35.8
|
GB6479 10#
|
|
|
|
STB410
(STB42)
|
ASTM A178 C
A210 A1
|
DIN 17175 ST45.8
|
GB5310 20G
GB6479 20G
|
|
|
|
STB510
|
ASTM A210 C
|
DIN 17175 19Mn5
|
|
|
锅炉、热交换器用合金管管
|
JIS G3462
|
STBA20
|
ASTM A213 T2
|
|
GB9948 GB5310 GB6479 12CrMo
|
|
|
|
STBA22
|
ASTM A213 T12
|
DIN 17175 13CrMo44
|
GB9948 GB5310 GB6479 15CrMo
|
|
|
|
STBA23
|
ASTM A213 T11
A199 T11
|
|
|
|
|
|
STBA24
|
ASTM A213 T22
A199 T22
|
DIN 17175 10CrMo910
|
GB5310 12Cr2Mo
GB6479 12Cr2Mo
|
|
|
|
STBA25
|
ASTM A213 T5
A199 T5
|
DIN 17175 12CrMo195
|
GB9948 1Cr5Mo
GB6479 1Cr5Mo
|
|
|
|
STBA26
|
ASTM A213 T9
A199 T9
|
DIN 17175 X12CrMo91
|
|
|
加热炉用钢管
|
JIS G3467
|
STFA410
|
|
|
GB9948 20#
|
|
|
|
STFA23
|
ASTM A200 T11
|
|
|
|
|
|
STFA24
|
ASTM A200 T22
|
|
|
|
|
|
STFA25
|
ASTM A200 T5
|
|
GB9948 1Cr5Mo
|
|
|
|
STFA26
|
ASTM A200 T9
|
|
|
梧州耐高温不锈钢管现货
| 不锈钢管 | 齐全 | 65×6-12 | 电议 | 大量 | 大量 | 电议 | 电议 |
| 不锈钢管 | 齐全 | 89×6-12 | 电议 | 大量 | 大量 | 电议 | 电议 |
| 不锈钢管 | 齐全 | 180×8 | 电议 | 大量 | 大量 | 电议 | 电议 |
| 不锈钢管 | 齐全 | 185×18 | 电议 | 大量 | 大量 | 电议 | 电议 |
| 不锈钢管 | 齐全 | 194×16 | 电议 | 大量 | 大量 | 电议 | 电议 |
| 不锈钢管 | 齐全 | 196×16 | 电议 | 大量 | 大量 | 电议 | 电议 |
梧州耐高温不锈钢管知识
GJB2294航空用不锈钢及耐热钢棒规范,本规范规定了航空用不锈及耐热钢棒的分类、技术要求、质量保证规定、交货准备等内容。本规范适用于航空用尺寸不大于250mm锻制、札制和冷拉的不锈及耐热钢棒。钢棒按组织特征分为奥氏体型、奥氏体铁素体型、铁素体型、珠光体型、马氏体型和沉淀硬化型等六类钢棒按交货状态分为：锻制、轧制和冷拉钢棒；锻制、轧制和冷拉后经热处理(退火、回火、固溶等)钢棒。根据需方要求，切削加工用奥氏体型、奧氏体铁素体型、沉淀硬化型钢棒可进行固溶处理。钢棒交货状态应在合同中注明。钢棒按使用加工方法分为：压力加工(热压.力加工和冷压力加工)用钢棒和切削加工用钢棒。钢棒的使用加工方法应在合同中注明，未注明时按切削加工用钢棒交货。钢棒按表面状态分为：锻制或轧制表面；冷拉表面；酸洗或喷砂表面；剥皮表面；车光或银亮表面。订货合同未注明时，按锻制、轧制或冷拉表面，其它要求必须在合同中注明。
热处理状态交货钢棒，其硬度应符合标准的规定。冷拉状态钢棒的硬度由供需双方协商规定。在交货的钢棒上切取试样毛坯，经热处理后制成试样测定力学性能应符合标准的规定。对固溶状态交货的钢棒，其试样毛坯不再进行固溶处理。标准中所列力学性能对沉淀硬化型钢仅适应于尺寸不大于75mm的钢棒，其它类型钢仅适应于尺寸不大于100mm的钢棒。对尺寸大于75mm和100mm的钢棒,可相应改锻成60～75mm和80～100mm样坯上测定力学性能或按供需双方协商规定。