兰州Q345b无缝钢管新闻
|
用途
|
日本
|
美国
|
德国
|
中国
|
|
锅炉、热交换器用碳素钢钢管
|
JIS G3461
|
STB340
(STB35)
|
ASTM A179
A192
|
DIN 17175 ST35.8
|
GB6479 10#
|
|
|
|
STB410
(STB42)
|
ASTM A178 C
A210 A1
|
DIN 17175 ST45.8
|
GB5310 20G
GB6479 20G
|
|
|
|
STB510
|
ASTM A210 C
|
DIN 17175 19Mn5
|
|
|
锅炉、热交换器用合金管管
|
JIS G3462
|
STBA20
|
ASTM A213 T2
|
|
GB9948 GB5310 GB6479 12CrMo
|
|
|
|
STBA22
|
ASTM A213 T12
|
DIN 17175 13CrMo44
|
GB9948 GB5310 GB6479 15CrMo
|
|
|
|
STBA23
|
ASTM A213 T11
A199 T11
|
|
|
|
|
|
STBA24
|
ASTM A213 T22
A199 T22
|
DIN 17175 10CrMo910
|
GB5310 12Cr2Mo
GB6479 12Cr2Mo
|
|
|
|
STBA25
|
ASTM A213 T5
A199 T5
|
DIN 17175 12CrMo195
|
GB9948 1Cr5Mo
GB6479 1Cr5Mo
|
|
|
|
STBA26
|
ASTM A213 T9
A199 T9
|
DIN 17175 X12CrMo91
|
|
|
加热炉用钢管
|
JIS G3467
|
STFA410
|
|
|
GB9948 20#
|
|
|
|
STFA23
|
ASTM A200 T11
|
|
|
|
|
|
STFA24
|
ASTM A200 T22
|
|
|
|
|
|
STFA25
|
ASTM A200 T5
|
|
GB9948 1Cr5Mo
|
|
|
|
STFA26
|
ASTM A200 T9
|
|
|
兰州Q345b无缝钢管知识
316L不锈钢管
316L不锈钢的最大碳含量0.03,可用于焊接后不能进行退火和需要最大耐腐蚀性的用途中。
316L不锈钢管 316和317不锈钢（317不锈钢的性能见后）是含钼不锈钢种。
317不锈钢中的钼含量略高明于316不锈钢.由于钢中钼，该钢种总的性能优于310和304不锈钢，高温条件下，当硫酸的浓度低于15％和高于85％时，316不锈钢具有广泛的用途。
316不锈钢还具有良好的而氯化物侵蚀的性能，所以通常用于海洋环境。
耐腐蚀性
耐腐蚀性能优于304不锈钢，在浆和造纸的生产过程中具有良好的耐腐蚀的性能。
而且316不锈钢还耐海洋和侵蚀性工业大气的侵蚀。耐热性 在1600度以下的间断使用和在1700度以下的连续使用中，316不锈钢具有好的耐氧化性能。
在800-1575度的范围内，最好不要连续作用316不锈钢，但在该温度范围以外连续使用316不锈钢时，该不锈钢具有良好的耐热性。
316L不锈钢的耐碳化物析出的性能比316不锈钢更好，可用上述温度范围。
热处理
在1850-2050度的温度范围内进行退火，然后迅速退火，然后迅速冷却。
316不锈钢不能过热处理进行硬化。
焊接
316不锈钢具有良好的焊接性能。可采用所有标准的焊接方法进行焊接。焊接时可根据用途，分别采用316Cb、316L或309Cb不锈钢填料棒或焊条进行焊接。为获得最佳的耐腐蚀性能，316不锈钢钢的焊接断面需要进行焊后退火处理。如果使用316L不锈钢，不需要进行焊后退火处理。
典型用途
纸浆和造纸用设备热交换器、染色设备、胶片冲洗设备、管道、沿海区域建筑物外部用材料
兰州Q345b无缝钢管现货
| 不锈钢管 | 齐全 | 185×18 | 电议 | 大量 | 大量 | 电议 | 电议 |
| 不锈钢管 | 齐全 | 219×15 | 电议 | 大量 | 大量 | 电议 | 电议 |
| 不锈钢管 | 齐全 | 273×6-12 | 电议 | 大量 | 大量 | 电议 | 电议 |
| 不锈钢管 | 齐全 | 273×34 | 电议 | 大量 | 大量 | 电议 | 电议 |
| 不锈钢管 | 齐全 | 325×8-10 | 电议 | 大量 | 大量 | 电议 | 电议 |
| 不锈钢管 | 齐全 | 508×15 | 电议 | 大量 | 大量 | 电议 | 电议 |
贵州华冶钢联管材有限公司
电 话：0851-87975109
手 机：13985191185
联系人：孙先生
|